NORYL™ EXNL1117 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z2ynB7_NORYL-EXNL1117-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| high gloss NORYL |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.12 | g/cm³ | ASTM D792 |
| -- | 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 25.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.060 | % | |
| Equilibrium, 23°C, 50% RH | 9.0E-3 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2560 | MPa | ASTM D638 |
| -- | 2810 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 67.0 | MPa | ASTM D638 |
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Break 3 | 55.0 | MPa | ASTM D638 |
| Break | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 3.6 | % | ASTM D638 |
| Yield | 3.3 | % | ISO 527-2/50 |
| Break 5 | 5.2 | % | ASTM D638 |
| Break | 4.4 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2730 | MPa | ASTM D790 |
| -- 7 | 2650 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 100 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 20 | J/m | ASTM D256 |
| 23°C | 85 | J/m | ASTM D256 |
| -30°C 10 | 4.6 | kJ/m² | ISO 180/1A |
| 23°C 11 | 9.3 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 30.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 75.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 75.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 96.0 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 98.0 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.9E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, Testing by SABIC | V-1 | ||
| 2.50 mm, Testing by SABIC | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 to 82.2 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 216 to 266 | °C | |
| Middle Temperature | 227 to 271 | °C | |
| Front Temperature | 238 to 277 | °C | |
| Nozzle Temperature | 249 to 277 | °C | |
| Processing (Melt) Temp | 249 to 277 | °C | |
| Mold Temperature | 54.4 to 76.7 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® P270 | Nilit Plastics | Nylon 66 | POLYNIL® |
| Sindustris POM N110LD | Sincerity Australia Pty Ltd. | Acetal (POM) Homopolymer | Sindustris POM |
| Cellophane™ 360MSB | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Infino TH-1100 | SAMSUNG SDI CO., LTD. | PC | Infino |
| ESTOPLAST XU 6315GY02 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |