Radel® R-5900
| Category: | PPSU , Polyphenylsulfone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Radel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z1eGs2_Radel-R-5900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Radel® R-5900 polyphenylsufone (PPSU) offers medium melt viscosities for long flow lengths and greater injection molding ease. It also provides exceptional hydrolytic stability and toughness that is superior to that of other commercially available, high-temperature engineering resins. It offers high deflection temperature and outstanding resistance to environmental stress cracking. The resin is inherently flame retardant and has excellent thermal stability and good electrical properties.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (365°C/5.0 kg) | 26 to 36 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.37 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.18 mm) | 2340 | MPa | ASTM D638 |
| Tensile Strength (3.18 mm) | 70.3 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18 mm | 7.2 | % | |
| Break, 3.18 mm | 60 to 120 | % | |
| Flexural Modulus (3.18 mm) | 2340 | MPa | ASTM D790 |
| Flexural Strength (5.0% Strain, 3.18 mm) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 207 | °C | ASTM D648 |
| Glass Transition Temperature | 220 | °C | ASTM E1356 |
| CLTE - Flow (3.18 mm) | 5.6E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm, ALL) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 360 to 391 | °C | |
| Mold Temperature | 138 to 163 | °C | |
| Screw Compression Ratio | 2.2:1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 171 | °C | |
| Drying Time | 4.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 258P1 BLACK 2N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| BorSafe™ HE3476-LS | Borealis AG | HDPE | BorSafe™ |
| FRAGOM LC/125 RR | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| En Chuan 6013WAL | En Chuan Chemical Industries Co,. Ltd. | Polyester, TS | En Chuan |
| Sylvin 9302-70 FU White 1327 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |