Next Nylon 6 Prime Series NGF2 20-01GY
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z13qaw_Next-Nylon-6-Prime-Series-NGF2-20-01GY.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA6 Glass Fiber Reinforced FR Grey Compound (Halogen & Phosphorous free) Product Applications This grade is used for Electrical and Electronics industries such as Switch parts coil former, Energy meter parts MCB Housing etc Benefits Good Flow and processability & excellent combination between electrical and Mechanical property. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.32 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 1.0 | -- | % | |
| Across Flow | 0.60 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 2.0 | -- | % | |
| Saturation 1 | 6.5 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 110 | -- | ||
| R-Scale | 120 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5800 | -- | MPa | ASTM D638 |
| Tensile Strength | 120 | 80.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | 7.0 | % | ASTM D638 |
| Flexural Modulus | 5600 | 2400 | MPa | ASTM D790 |
| Flexural Strength | 180 | 150 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 78 | 120 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 210 | -- | °C | |
| 1.8 MPa, Unannealed | 170 | -- | °C | |
| Melting Temperature | 220 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.800 mm) | 750 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 250 to 260 | °C | |
| Middle Temperature | 260 to 270 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Mold Temperature | 65.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIME TPO R110MP | Prime Polymer Co., Ltd. | PP Impact Copolymer | PRIME TPO |
| SEETEC LDPE XJ800 | Lotte Chemical Corporation | LDPE | SEETEC LDPE |
| Sindustris ABS LSH721S | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Westlake LDPE EF796 | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| FRAGOM PR/420 NAT P | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |