Leona™ CR301
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z0oNaX_Leona-CR301.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ CR301 is a Polyamide 66 (Nylon 66) product filled with mineral. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ CR301 include electrical/electronic applications and industrial applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.48 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 0.50 to 1.3 | -- | % | Internal Method |
| Water Absorption | ||||
| Saturation, 23°C | -- | 1.5 | % | |
| Equilibrium, 23°C, 50% RH | -- | 1.5 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | -- | ASTM D785, ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 7000 | 4100 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Break, 23°C | 85.0 | 59.0 | MPa | ISO 527-2 |
| -- | 88.0 | 64.0 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Break | 3.0 | 3.5 | % | ASTM D638 |
| Break, 23°C | 2.0 | 11 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 5900 | 2900 | MPa | ASTM D790 |
| 23°C | 7400 | 4100 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 147 | 93.0 | MPa | ASTM D790 |
| 23°C | 140 | 92.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles) | -- | 8.00 | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 51 | 90 | kJ/m² | ISO 179 |
| Notched Izod Impact | 34 | 39 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 249 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 191 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 188 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 4.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | HB | -- | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOND 3012 | SILON s.ro | LLDPE | TABOND |
| TROSIFOL® Sound Control+ | Kuraray Co., Ltd. | PVB | TROSIFOL® |
| Trexprene® A75SCI-HF | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| TORZEN® HV240A NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Hostacom AJ 1165 E BLACK | LyondellBasell Industries | PP Copolymer | Hostacom |