ULTEM™ HU1000 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z0b5nS_ULTEMHU1000resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent, standard flow Polyetherimide (Tg 217C). RoHS compliant. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. UL94 V0 and 5VA listed. EtO and steam sterilizable. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 9.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/5.0 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | |||
| 24 hr | 0.25 | % | ASTM D570 |
| Saturated, 23°C | 1.3 | % | ISO 62 |
| Equilibrium, 23°C | 1.3 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.70 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3580 | MPa | ASTM D638 |
| -- | 3200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 110 | MPa | ASTM D638 |
| Yield | 105 | MPa | ISO 527-2/5 |
| Fracture 3 | 90.0 | MPa | ASTM D638 |
| Fracture | 85.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 7.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/5 |
| Fracture 5 | 60 | % | ASTM D638 |
| Fracture | 60 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 3440 | MPa | ASTM D790 |
| -- 7 | 3300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 160 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 173 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 55 | J/m | ASTM D256 |
| 23°C | 53 | J/m | ASTM D256 |
| -30°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 1300 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 201 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 215 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 219 | °C | ASTM D1525 13 |
| -- | 215 | °C | ISO 306/B50 |
| -- | 211 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -20 to 150°C | 5.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -20 to 150°C | 5.4E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Air | 33 | kV/mm | ASTM D149 |
| 1.60 mm, in Oil | 28 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.15 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 1.3E-3 | ASTM D150 | |
| 2.45 GHz | 2.5E-3 | ASTM D150 | |
| Arc Resistance 14 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 47 | % | ASTM D2863 |
| NBS Smoke Density - Flaming, Ds, 4 min | 0.700 | ASTM E662 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 332 - 399 | °C | |
| Middle Temperature | 338 - 399 | °C | |
| Front Temperature | 343 - 399 | °C | |
| Nozzle Temperature | 343 - 399 | °C | |
| Processing (Melt) Temp | 349 - 399 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| 14 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Beetle® PET110 | Teknor Apex Company (Chem Polymer) | PET | Beetle® |
| ESTAPROP 0540 GFC V0 | Cossa Polimeri S.r.l. | PP, Unspecified | ESTAPROP |
| Hostaform® SlideX™ C0304 XAP² ™ | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Petrothene® LT543501 | LyondellBasell Industries | HDPE | Petrothene® |
| POCAN® S 7926 000000 | LANXESS GmbH | PBT | POCAN® |