Fiberfil® J-60/40
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YzPFYQ_Fiberfil-J-60-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fiberfil®J-60/40 is a polypropylene homopolymer (PP Homopoly) material, and the filler is 40% glass fiber reinforced material. This product is available in North America,. Fiberfil®The main characteristics of J-60/40 are: homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.20 | % | ASTM D955 |
| 6.35 mm | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7580 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 72.4 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 6890 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 157 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 149 | °C | ASTM D648 |
| Additional Information |
|---|
| Rockwell Hardness, ASTM D785, R-Scale: 100 to 110 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 59 T 40 LW 031 | Plastcom | PP, Unspecified | SLOVALEN® |
| Amilan® CM2402 | Toray Resin Company | Nylon 610 | Amilan® |
| KRATON® D1192 A | Kraton Polymers LLC | SBS | KRATON® |
| Hostacom PP HH42L 356015 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| LEXAN™ 4704 resin | SABIC Innovative Plastics | PPC | LEXAN™ |