VENYL UWGB300H
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YxWlVe_VENYL-UWGB300H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL UWGB300H is a 30% glass fibre/bead reinforced polyamide 66 intended for Injection moulding. APPLICATIONS VENYL UWGB300H has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. VENYL UWGB300H is available in both natural and black (VENYL UWGB300H BLACK 8229) but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 to 0.90 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 174 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.2 | % | ISO 527-2 |
| Flexural Modulus | 6900 | MPa | ISO 178 |
| Flexural Stress | 265 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 29 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 245 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+14 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Oxygen Index | 23 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 285 to 300 | °C | |
| Middle Temperature | 280 to 295 | °C | |
| Front Temperature | 275 to 290 | °C | |
| Nozzle Temperature | 265 to 280 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 701 HF | RTP Company | HDPE | RTP |
| SUPREME Specialty PS SP256 | Supreme Petrochem Ltd. | PS (Specialty) | SUPREME Specialty PS |
| Topilene® J642 | Hyosung Corporation | PP Impact Copolymer | Topilene® |
| Bergamid™ XP6042701 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Elastocon® SMR1555 | Elastocon TPE Technologies | TPO (POE) | Elastocon® |