Stamylex® 2H 568
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Stamylex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YwepNU_Stamylex-2H-568.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stamylex® 2H 568 is an octene based linear low density polyethylene produced in a solution polymerisation process using a Ziegler - Natta catalyst. This grade contains an additive package for thermal stabilization. Stamylex 2H 568 is especially designed for the production of non wovens. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.930 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.9 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 395 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 10.0 | MPa | ISO 527-2/500 |
| Tensile Strain (Break) | 150 | % | ISO 527-2/500 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 105 | °C | ISO 306/A |
| Melting Temperature | 124 | °C | ASTM D3418 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC6GPN (Series: GP/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| WELLAMID Nylon 6600 GS 15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Cri-Line SP-612 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Flexirene® CL 10 U | Versalis S.p.A. | LLDPE | Flexirene® |
| POFEX 8200EP85M | POLYROCKS CHEMICAL CO., LTD | TPE | POFEX |