LNP™ LUBRICOMP™ LCL33 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YwZGTL_LNPLUBRICOMPLCL33compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP LCL33 is a compound based on Polyethereketone resin containg Carbon Fiber, PTFE. Added features include: Elecrtically Conductive , Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound LCL-4033 Product reorder name: LCL33 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (400°C/10.0 kg) | 6.00 - 8.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 162 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.9 | % | ISO 527-2/5 |
| Flexural Modulus 1 | ISO 178 | ||
| -- | 10700 | MPa | ISO 178 |
| 80°C | 10300 | MPa | ISO 178 |
| 120°C | 10200 | MPa | ISO 178 |
| 150°C | 5700 | MPa | ISO 178 |
| 200°C | 3000 | MPa | ISO 178 |
| 250°C | 2.60 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 223 | MPa | ISO 178 |
| -- 4 | 255 | MPa | ISO 178 |
| 80°C 5 | 192 | MPa | ISO 178 |
| 120°C 6 | 158 | MPa | ISO 178 |
| 150°C 7 | 100 | MPa | ISO 178 |
| 200°C 8 | 60.0 | MPa | ISO 178 |
| 250°C 9 | 50.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.35 | ASTM D3702 Modified | |
| With Self-Static | 0.28 | ASTM D3702 Modified | |
| Flexural Strain at Break 10 | ISO 178 | ||
| -- | 2.7 | % | ISO 178 |
| 80°C | 2.7 | % | ISO 178 |
| 120°C | 2.7 | % | ISO 178 |
| 150°C | 6.0 | % | ISO 178 |
| 200°C | 6.3 | % | ISO 178 |
| 250°C | 6.5 | % | ISO 178 |
| Wear Factor - Washer | 17.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 11(23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 12(23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 13(1.8 MPa, Unannealed, 64.0 mm Span) | > 300 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 9.5E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 5.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 - 1.0E+5 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 349 - 360 | °C | |
| Middle Temperature | 366 - 377 | °C | |
| Front Temperature | 382 - 393 | °C | |
| Processing (Melt) Temp | 382 - 388 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | Yield |
| 6 . | Yield |
| 7 . | Yield |
| 8 . | Yield |
| 9 . | Yield |
| 10 . | 2 mm/min |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® FG02 | Guangdong Silver Age Sci & Tech. Co., Ltd | PVC, Rigid | SILVER® |
| Sylvin 8707-84 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polystyrene Impact 825 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| Bormed™ RG835MO | Borealis AG | PP Random Copolymer | Bormed™ |
| GAPEKK™ 3200P | Gharda Chemicals Ltd. | PEKK | GAPEKK™ |