HAIPLEN EP10 G3 BA
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YwVuLa_HAIPLEN-EP10-G3-BA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene copolymer 15% glass fibres reinforced chemically coupled, medium low flow. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.40 - 0.60 | % | Internal method |
| Flow direction | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 56.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2800 | MPa | ISO 178 |
| Flexural Stress 2 | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 125 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index | 20 | % | ASTM D2863 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 3(600°C) | 15 | % | ISO 3451 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Pre-heat Temperature: 70 to 80°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | 1 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) M/HI | A. Schulman Europe | ABS | POLYMAN® |
| Vyncolit® RX®3-2-520F | Vyncolit N.V. | DAP | Vyncolit® |
| Bayflex® 180 RRIM (20% Mica) | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| Karina IVORY PVC COMPOUND 75920-35/ 1-DY-AC (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 916VO-70C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |