UmaPET LO/LI Datasheet,PET,Ester Industries Ltd.-SHANGHAI SUSHENG

Message
Key Features UmaPET LO/LI is transparent film with one-side chemical treated for improved adhesion properties in metallization and printing / lamination processes. The film possesses excellent thermal, mechanical, optical and surface properties along with excellent transparency and dimensional stability. APPLICATIONS LO/LI film is widely used for high metal adhesion requirement in metallizing. Shows excellent ink and adhesive adhesion performance in printing and lamination which results in excellent interlayer bond strength in laminates.

General Information
Features	Excellent Printability Good Adhesion Good Dimensional Stability Good Surface Finish High Clarity Metallizable Opticals
Uses	Film Laminates
Appearance	Clear/Transparent
Forms	Film

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D1204
Flow : 150°C, 30 min, 0.0100 mm	2.5	%
Flow : 150°C, 30 min, 0.0120 mm	2.5	%
Flow : 150°C, 30 min, 0.0150 mm	2.5	%
Flow : 150°C, 30 min, 0.0230 mm	2.5	%
Across Flow : 150°C, 30 min, 0.0100 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0120 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0150 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0230 mm	0.40	%

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
vs. Itself - Dynamic ¹	0.50
vs. Itself - Dynamic ²	0.50
vs. Itself - Dynamic ³	0.50
vs. Itself - Dynamic ⁴	0.42
vs. Itself - Static ⁵	0.45
vs. Itself - Static ⁶	0.45
vs. Itself - Static ⁷	0.45
vs. Itself - Static ⁸	0.48

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	10 12 15 23	µm
Film Thickness - Recommended / Available	10, 12, 15, 23 µm
Tensile Strength			ASTM D882
MD : Break, 10 µm	206	MPa
MD : Break, 12 µm	206	MPa
MD : Break, 15 µm	186	MPa
MD : Break, 23 µm	186	MPa
TD : Break, 10 µm	216	MPa
TD : Break, 12 µm	216	MPa
TD : Break, 15 µm	206	MPa
TD : Break, 23 µm	206	MPa
Tensile Elongation			ASTM D882
MD : Break, 10 µm	100	%
MD : Break, 12 µm	100	%
MD : Break, 15 µm	100	%
MD : Break, 23 µm	100	%
TD : Break, 10 µm	90	%
TD : Break, 12 µm	90	%
TD : Break, 15 µm	90	%
TD : Break, 23 µm	90	%
Yield			Internal Method
10.0 µm	71.4	m²/kg
12.0 µm	59.5	m²/kg
15.0 µm	47.6	m²/kg
23.0 µm	31.0	m²/kg

Additional Information	Nominal Value	Unit	Test Method
Wetting Tension			ASTM D2578
Coated side : 10.0 µm	48	dyne/cm
Coated side : 12.0 µm	48	dyne/cm
Coated side : 15.0 µm	48	dyne/cm
Coated side : 23.0 µm	48	dyne/cm
Plain side : 10.0 µm	42	dyne/cm
Plain side : 12.0 µm	42	dyne/cm
Plain side : 15.0 µm	42	dyne/cm
Plain side : 23.0 µm	42	dyne/cm

Optical	Nominal Value	Unit	Test Method
Haze			ASTM D1003
10.0 µm	3.5	%
12.0 µm	3.5	%
15.0 µm	3.5	%
23.0 µm	4.5	%

Category:	PET , Polyethylene Terephthalate
Manufacturer:	Ester Industries Ltd.
Trademark:	UmaPET
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	YuSDMg_UmaPET-LO-LI.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
ADMER™ NF528A	Mitsui Chemicals America, Inc.	PE, Unspecified	ADMER™
ALCOM® TCD PA66 5040 14015	ALBIS PLASTIC GmbH	Nylon 66	ALCOM® TCD PA66
FHR EPS R-MER II® 5627 (1.25 lb/ft³)	Flint Hills Resources, LP	PS (EPS)	FHR EPS
Geon™ Bold L5000	PolyOne Corporation	PVC Alloy	Geon™ Bold
Innothane® FM-110	Innovative Polymers, Inc.	TSU	Innothane®