Nycal™ 2060H
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Technical Polymers, LLC |
| Trademark: | Nycal™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Yr4BEa_Nycal-2060H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nycal™2060H is a polyamide 612 (nylon 6/12) material,. This product is available in North America and is processed by extrusion or injection molding. Nycal™The main features of 2060H are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 58.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 30 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2240 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 135 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 57.2 | °C | ASTM D648 |
| Melting Temperature | 218 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Tensile Elongation, ASTM D638: >30%Volum Resistivity, ASTM D257: >1e13 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.9 - 79.4 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 232 - 277 | °C | |
| Mold Temperature | 48.9 - 93.3 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.103 - 0.689 | MPa | |
| Screw Speed | 100 | rpm | |
| Clamp Tonnage | 3.4 - 5.5 | kN/cm² | |
| Cushion | 3.18 - 12.7 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® M26500 | Reliance Industries Limited | LLDPE | RELENE® |
| RAMSTER RF300G4 | Polyram Ram-On Industries | PBT | RAMSTER |
| Geon™ Vinyl Flexible C70U0 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| MAJORIS AG200E - 8229 | AD majoris | HDPE | MAJORIS |
| SCHULAKETON HV 4DE | A. Schulman Europe | PK-Aliphatic | SCHULAKETON |