LG ABS ER460
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Yqhwxk_LG-ABS-ER460.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG ABS ER460 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. The main features of LG ABS ER460 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 23 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2160 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 48.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 50 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 255 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 78.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 120 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 110 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 250 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 250 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 96.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 91.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 97.0 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 - 200 | °C | |
| Middle Temperature | 190 - 210 | °C | |
| Front Temperature | 200 - 220 | °C | |
| Nozzle Temperature | 200 - 230 | °C | |
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C | |
| Back Pressure | 29.4 - 58.8 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.01% |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 700 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Thanelene® TPU S90A15 PRTA010 TP304 MSP | Petropol Industry and Trade of Polymers LTDA | TPU-Polyester | Thanelene® TPU |
| Generic PP Homopolymer - Calcium Carbonate | Generic | PP Homopolymer | Generic |
| Hostacom GP621-2 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Sylvin 8980-60 White 1323 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |