Romiloy® 4010/07
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Romiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YqVN7q_Romiloy-4010-07.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Romiloy®4010/07 is an acrylonitrile butadiene styrene nylon (ABS nylon) material,. This product is available in Europe, and the processing method is injection molding. Romiloy®The main features of 4010/07 are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 43.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 100 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 1700 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 19 | kJ/m² | ISO 179/1eA |
| 23°C | 72 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 107 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| Tensile Strain @ Break, DIN EN ISO 527, 50 mm/min, 23°C: >100% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 230 - 250 | °C | |
| Front Temperature | 230 - 250 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 50.0 - 90.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 1.00 | MPa | |
| Screw Speed | 12 - 18 | rpm |
| Injection instructions |
|---|
| Holding Pressure: moderate to high |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 19HT30-0.002 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| TORZEN® T2000HSL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Borealis PP HF136MO | Borealis AG | PP Homopolymer | Borealis PP |
| Geon™ Vinyl Flexible H43356A | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Petrothene® NA204000 (Injection) | LyondellBasell Industries | LDPE | Petrothene® |