SCHULAMID® 612 FS 4104
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ypgcv7_SCHULAMID-612-FS-4104.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High impact modified Polyamide 612 with electrical neutral heat stabilization |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.01 | -- | g/cm³ | ISO 1183/A |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1200 | 320 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 40.0 | 30.0 | MPa | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 200 | > 250 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 110 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 110 kJ/m² | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 70.0 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 55.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 200 | -- | °C | ISO 306/A50 |
| -- | 100 | -- | °C | ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 30 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | IEC 60695-11-10, -20 | |
| 3.00 mm | HB | -- | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 725 | -- | °C | IEC 60695-2-12 |
| 3.00 mm | 725 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 750 | -- | °C | IEC 60695-2-13 |
| 3.00 mm | 750 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 ISO 1874-PA 612-EAGHLW-12-010-NDIN73378-PA 612-HIHL |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1002 HI | RTP Company | PBT | RTP |
| Hanwha Total PP BI45W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| HONES® PA66 GF35 | Guangdong Shunde Hones Polymer Material Co., Ltd. | Nylon 66 | HONES® |
| Karina IVORY PVC COMPOUND -E 832-35/ 1-Y-ERYB-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OXNILON 6 4IMP | Oxford Polymers | Nylon 6 | OXNILON 6 |