Ryton® XE5515BL
| Category: | PPS Alloy , Polyphenylene Sulfide Alloy |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Ryton® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YpeFEq_Ryton-XE5515BL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ryton® XE5515BL 15% glass fiber reinforced polyphenylene sulfide alloy compound provides excellent mechanical strength and chemical resistance at elevated temperatures and is suitable for extrusion or blow molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (316°C/5.0 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 3.20 mm | 0.50 | % | |
| Across Flow : 3.20 mm | 0.60 | % | |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 118 | ||
| R-Scale | 87 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 6210 | MPa | ASTM D638 |
| -- | 5800 | MPa | ISO 527-2 |
| Tensile Strength | |||
| -- | 103 | MPa | ASTM D638 |
| -- | 110 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 2.9 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 5520 | MPa | ASTM D790 |
| -- | 5500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 159 | MPa | ASTM D790 |
| -- | 170 | MPa | ISO 178 |
| Poisson's Ratio | 0.41 | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 3.18 mm | 96 | J/m | ASTM D256 |
| -- | 10 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact | |||
| 3.18 mm | 690 | J/m | ASTM D4812 |
| -- | 45 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 190 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -50 to 50°C | 3.0E-5 | cm/cm/°C | |
| Flow : 100 to 200°C | 2.0E-5 | cm/cm/°C | |
| Transverse : -50 to 50°C | 5.5E-5 | cm/cm/°C | |
| Transverse : 100 to 200°C | 9.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.23 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 24 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 25°C, 1 kHz | 3.60 | ||
| 25°C, 1 MHz | 3.50 | ||
| Dissipation Factor | ASTM D150 | ||
| 25°C, 1 kHz | 2.0E-3 | ||
| 25°C, 1 MHz | 5.0E-3 | ||
| Arc Resistance | 100 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 150 | V | UL 746 |
| Insulation Resistance 1(90°C) | 1.0E+13 | ohms |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by CP Chemical) | V-0 | UL 94 | |
| Oxygen Index | 50 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | 95%RH, 48 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Jiangsu Sinarise JM9013 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Plenco 04466 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |
| Braskem PP 5D49 | Braskem America Inc. | PP Homopolymer | Braskem PP |
| ESTOPLAST XU 6100BL15 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |
| NORYL™ NH4030B resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |