Order Products : sales@su-jiao.com
Lastilac 11 G/10
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Lastilac |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YoZhZL_Lastilac-11-G-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ABS/PC Blend (ABS/PC) based compound. Glass fibres. Good surface appearance. Good impact resistance. Good thermal properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.50 to 0.70 | % | |
| Flow : 2.00 mm | 0.45 to 0.65 | % | |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 3900 | MPa | |
| 60°C | 3600 | MPa | |
| 90°C | 3300 | MPa | |
| 120°C | 1300 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 60°C | 50.0 | MPa | |
| Yield, 90°C | 30.0 | MPa | |
| Yield, 120°C | 15.0 | MPa | |
| Break, 23°C | 60.0 | MPa | |
| Break, 60°C | 50.0 | MPa | |
| Break, 90°C | 23.0 | MPa | |
| Break, 120°C | 5.00 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 60°C | 2.0 | % | |
| Yield, 90°C | 2.0 | % | |
| Yield, 120°C | 2.0 | % | |
| Break, 23°C | 2.5 | % | |
| Break, 60°C | 3.0 | % | |
| Break, 90°C | 6.0 | % | |
| Break, 120°C | 70 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 12 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 35 | kJ/m² | |
| 23°C | 25 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 115 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 115 | °C | |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 350 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 15 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer S80U | Precision Polymer Engineering Ltd. | Silicone | Precision Polymer |
| TECAST™ 6PAM | Ensinger Inc. | Nylon 6 | TECAST™ |
| NuSil MED-4765 | NuSil Technology | Rubber | NuSil |
| ADMER™ QF500A | Mitsui Chemicals America, Inc. | PP, Unspecified | ADMER™ |
| Globalene® PT101N | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |