Witcom PA66 4L1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YmZWM2_Witcom-PA66-4L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PA66 4L1 is a polyamide 66 (nylon 66) product,. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 1.3 - 1.8 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 6.8 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 8.0 | % | ISO 527-2 |
| Flexural Modulus | 2800 | MPa | ISO 178 |
| Flexural Stress | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 5.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 75 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | °C | ISO 75-2/A |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 90.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | ISO 1210 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 275 - 295 | °C | |
| Mold Temperature | 60.0 - 95.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 1.00 | MPa |
| Injection instructions |
|---|
| Screw speed: 0.1 to 0.2 m/sInjection pressure: Keep to a minimumHold pressure: Keep to a minimum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 204A HS | RTP Company | Nylon 6 | RTP |
| Karina CLEAR PVC COMPOUND -E 80/235-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ DX02437 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |
| PermaStat® 300 | RTP Company | PC | PermaStat® |
| Optix® CA-75 HID | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |