Teflon® AF 1600
| Category: | Fluoropolymer , Fluoropolymer |
| Manufacturer: | DuPont Fluoropolymers |
| Trademark: | Teflon® AF |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YmU2bN_Teflon-AF-1600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Teflon® AF is a family of amorphous fluoropolymers. These materials are similar to other amorphous polymers in optical clarity and mechanical properties, including strength. They also resemble fluoropolymers in their performance over a wide range of temperatures, outstanding electrical properties, and chemical resistance. They are distinct from other fluoropolymers in that they are soluble in selected solvents and have high gas permeability, high compressability, high creep resistance, and low thermal conductivity. They have the lowest dielectric constant of any known fluoropolymer. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.78 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 103 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 70°C | 70 | ||
| Shore D, 23°C | 77 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 26.4 to 28.4 | MPa | |
| Yield, 150°C | 0.800 to 12.6 | MPa | |
| 23°C | 25.4 to 28.4 | MPa | |
| 150°C | 1.60 to 13.8 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break, 23°C | 12 to 22 | % | |
| Break, 150°C | 76 to 100 | % | |
| Flexural Modulus | ASTM D790 | ||
| 23°C | 1700 to 1900 | MPa | |
| 150°C | 900 to 1100 | MPa | |
| Taber Abrasion Resistance (2000 Cycles) | 107 | mg |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability | 340 | Barrer | |
| Nitrogen Permeability | 130 | Barrer | |
| Water Permeation | 1140 | Barrer |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abbe Number | 92.0 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Contact Angle - with Water | 104 | ° | |
| Surface Energy | 16 | dyne/cm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 156 | °C | |
| 1.8 MPa, Unannealed | 154 | °C | |
| Glass Transition Temperature | 155 to 165 | °C | ASTM D3418 |
| CLTE - Flow | 2.6E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Dielectric Constant | 1.93 | ASTM D150 | |
| Dissipation Factor | 1.0E-4 to 2.0E-4 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.310 | ASTM D542 | |
| Transmittance | > 95.0 | % | ASTM D1003 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (250°C, 100 sec^-1) | 2660 | Pa·s | ASTM D3835 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE B5823 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| AKROMID® C3 GF 50 5 XTC natural (4946) | AKRO-PLASTIC GmbH | Nylon 66/6 | AKROMID® |
| Heramid® I/BGV 15c Black | Radici Plastics | Nylon 6 | Heramid® |
| INLUBE PCGF10TF15 | Infinity LTL Engineered Compounds | PC | INLUBE |
| Sylvin 3240-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |