LubriOne™ AT-30GF/15T NATURAL
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Yi9u8a_LubriOne-AT-30GF-15T-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PTFE lubricated |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.73 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 78.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 7150 | MPa | ASTM D790 |
| Flexural Strength 3 | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 52 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 145 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 190 - 200 | °C | |
| Middle Temperature | 190 - 200 | °C | |
| Front Temperature | 190 - 200 | °C | |
| Mold Temperature | 75.0 - 85.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® A3 GF 20 1 natural (1261) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Fainplast PVC GS 7004 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| ICORENE® N1018 | ICO Polymers EMEA, A Division of A. Schulman | EVA | ICORENE® |
| KEBAFORM® C 130 LS weiß | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| Badatech HT® PEEK 3111 GF 30 | Bada AG | PEEK | Badatech HT® |