Eraclene® MS 80 U
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Eraclene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YgtGkL_Eraclene-MS-80-U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eraclene MS 80 U is a gas phase high density polyethylene resin (HDPE) with antioxidants, suitable for injection moulding application. This grade has a narrow molecular weight distribution and a high fluidity make it ideally for injection moulding applications. The polymer has high thermal stability during extrusion and a good balance between fluidity and mechanical properties. Main Application Eraclene MS 80 U is an injection moulding grade designed for thin-walled (food containers) aerosol caps. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.955 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 27 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Compression Molded | 27.0 | MPa | |
| Break, Compression Molded | 10.0 | MPa | |
| Tensile Strain (Break, Compression Molded) | 100 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 1300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1(Compression Molded) | 40 | J/m | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 126 | °C | ISO 306/A |
| Melting Temperature | 135 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 to 260 | °C | |
| Middle Temperature | 190 to 260 | °C | |
| Front Temperature | 190 to 260 | °C | |
| Mold Temperature | 10.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDB 502-A Phillips Process | Marco Polo International, Inc. | HDPE | MARPOL® |
| Sinvicomp DBS5608 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| TRIREX® 3017IR | Samyang Corporation | PC | TRIREX® |
| ALTECH® PA66 A 2035/508 GF35 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Cevian®-V 720 | PlastxWorld Inc. | ABS | Cevian®-V |