Order Products : sales@su-jiao.com
GLS Blends MS309
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS Blends |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YgrxNi_GLS-Blends-MS309.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC /ABS Precolor |
| General Information | |
|---|---|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.00 to 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | > 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 45.0 to 50.0 | MPa | ASTM D638 |
| Flexural Modulus | 3000 to 3500 | MPa | ASTM D790 |
| Flexural Strength | 90.0 to 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 250 to 300 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 96.0 to 100 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 234 to 265 | °C | |
| Mold Temperature | 100 to 110 | °C | |
| Injection Pressure | 68.0 to 102 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® OBC 4955F | Teknor Apex Company | TPE | Telcar® |
| Sylvin 5204-75 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polystyrene Impact 4241 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| Exxtral™ Performance Polyolefin BNT010 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| LNP™ LUBRICOMP™ RP004 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |