Braskem PE LL6800N
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ygc51U_Braskem-PE-LL6800N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LL6800N resin is a Linear Low Density Polyethylene, copolymer of octene-1, produced by solution process, for blown film extrusion with excellent mechanical properties. It contains antiblock, processing aid and antioxidant additives. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 40.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 40.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 900 | % | |
| TD : Break, 25 µm, Blown Film | 1200 | % | |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant, MD : 25 µm, Blown Film | 180 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 200 | MPa | |
| Dart Drop Impact (25 µm, Blown Film) | 190 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 260 | g | |
| TD : 25 µm, Blown Film | 570 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 25.0 µm, Blown Film) | 103 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 14 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Elastollan® C95A10 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyester | Elastollan® |
| LEXAN™ HP2R resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Karina BLACK PVC COMPOUND 550-48/1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® PEEK CF10 GL10 TL10 A HF | Techmer Engineered Solutions | PEEK | Plaslube® |
| Sylvin 6239-85UV White 1583 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |