RTP ESD 4083 TFE 15 SI 2
| Category: | PPA , Polyphthalamide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YgLHaT_RTPESD4083TFE15SI2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Carbon Fiber - PTFE Lubricated - Silicone Lubricated - Electrically Conductive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.020 - 0.10 | % | ASTM D955 |
| Moisture Content | 0.050 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay | sec | FTMS 101C 4046.1 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17900 | MPa | ASTM D638 |
| Tensile Strength | 203 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.0 - 2.0 | % | ASTM D638 |
| Flexural Modulus | 14800 | MPa | ASTM D790 |
| Flexural Strength | 293 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 550 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 260 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | < 1.0E+4 | ohms | ESD STM11.11 |
| -- | < 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | < 1.0E+2 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.5 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Dew Point | -32 | °C | |
| Processing (Melt) Temp | 302 - 329 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Injection Pressure | 68.9 - 124 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SI302G15 | RJM International, Inc. | PET | RJM |
| SEMICOSIL® 927 F | Wacker Chemie AG | Silicone | SEMICOSIL® |
| Cellophane™ 400P | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| LOXIM 200 00 HB | LOXIM Industries Private Limited | PBT | LOXIM |
| API II ABS 920 | API II, Inc. | ABS | API II |