QR Resin QR-1018IM
| Category: | PC , Polycarbonate |
| Manufacturer: | QTR, Inc. |
| Trademark: | QR Resin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YgFesL_QR-Resin-QR-1018IM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
QR-1018IM is availible with UV (V) or Release (R). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 57.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 110 | % | ASTM D638 |
| Flexural Modulus | 2210 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 87.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed | 132 | °C | |
| 1.8 MPa, Unannealed | 127 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 254 to 277 | °C | |
| Middle Temperature | 266 to 288 | °C | |
| Front Temperature | 277 to 299 | °C | |
| Nozzle Temperature | 271 to 293 | °C | |
| Processing (Melt) Temp | 271 to 293 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® X6151 | Vyncolit N.V. | Phenolic | Vyncolit® |
| NYLEM® 66 GFR 20 | EMAS Plastik San.Tic.AS. | Nylon 66 | NYLEM® |
| FHR Polypropylene P9M6K-041A | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| LNP™ LUBRICOMP™ WL003 compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |
| Petrothene® GS707061 | LyondellBasell Industries | LLDPE | Petrothene® |