Premi-Glas® 3100-22 is a fiberglass reinforced thermoset bulk molding compound for electrical and flame retardant applications.

Good dimensional stability, including excellent thermal resistance.

Pigmentable for molded-in color; best appearance with mold texture.

Excellent property retention in cold and hot environments.

Recognized by Underwriters Laboratories, File # E42524.

Underwriters Laboratories 94-VO flame resistance at 1.5mm thickness.

General Information
Filler / Reinforcement	Glass Fiber
Additive	Flame Retardant
Features	Flame Retardant Good Colorability Good Dimensional Stability Medium Heat Resistance
Uses	Electrical/Electronic Applications
UL File Number	E42524
Forms	BMC - Bulk Molding Compound

Physical	Nominal Value	Unit
Specific Gravity	1.70 to 1.85	g/cm³
Molding Shrinkage - Flow	0.15 to 0.35	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (Compression Molded)	12400	MPa	ASTM D638
Tensile Strength (Compression Molded)	37.9	MPa	ASTM D638
Flexural Modulus (Compression Molded)	10300	MPa	ASTM D790
Flexural Strength (Compression Molded)	124	MPa	ASTM D790
Poisson's Ratio	0.30

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (Compression Molded)	430	J/m	ASTM D256
Unnotched Izod Impact (Compression Molded)	590	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
CLTE
Flow ¹	2.5E-5	cm/cm/°C
Transverse ²	3.5E-5	cm/cm/°C
Thermal Conductivity	0.30	W/m/K
RTI Elec	130	°C	UL 746
RTI Imp	130	°C	UL 746
RTI Str	130	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	15	kV/mm	ASTM D149
Arc Resistance	> 180	sec	ASTM D495
Comparative Tracking Index	600	V	ASTM D2303

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.52 mm)	V-0		UL 94

Injection	Nominal Value	Unit
Mold Temperature	149	°C
Injection Pressure	3.45 to 6.89	MPa

Note Message
1 .	XY Direction
2 .	Z Direction

Resin Grade	Manufacturer	Category	Trademark
Salflex 815C	Salflex Polymers Ltd.	PP Copolymer	Salflex
Miramid® VE25C	BASF Leuna GmbH	Nylon 6	Miramid®
Durez® 33763	Sumitomo Bakelite North America, Inc.	Phenolic	Durez®
LNP™ LUBRICOMP™ KL003 compound	SABIC Innovative Plastics	Acetal (POM) Copolymer	LNP™ LUBRICOMP™
LUVOCOM® 50-9022	Lehmann & Voss & Co.	PC	LUVOCOM®