LNP™ LUBRICOMP™ LCL36E compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YdzI0B_LNP-LUBRICOMP-LCL36E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP LCL36E is a compound based on Polyetheretherketone resin containing Carbon Fiber , PTFE. Added features include : Electrically Conductive, Internally Lubricated, Easy Molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 21600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 224 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 19800 | MPa | ISO 178 |
| Flexural Stress | 317 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | > 300 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 8.4E-6 | cm/cm/°C | |
| Transverse : 23 to 60°C | 4.2E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 349 to 360 | °C | |
| Middle Temperature | 366 to 377 | °C | |
| Front Temperature | 382 to 393 | °C | |
| Processing (Melt) Temp | 382 to 388 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X5575 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sylvin 9221-72 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® BKV 30 FN00 000000 | LANXESS Corporation | Nylon 6 | Durethan® |
| Mafill® CR CME 5144 | Ravago Group | PP Copolymer | Mafill® |
| 3M™ Dyneon™ PTFE Compound APNV063 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |