TABOREX TA 1104 HD
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SILON s.ro |
| Trademark: | TABOREX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YdLhhS_TABOREX-TA-1104-HD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A chemically-crosslinkable HDPE compound for the production of pipes for domestic hot and cold water, under floor heating and central heating application. TA 1104 HD is a crosslinkable compound made by Silane grafted ethylene polymer. This graft polymer constitutes together with a Masterbatch containing the crosslinking catalyst a "SIOPLAS-SYSTEM". Pipes produced with the SILON grade TA 1104 HD fulfil the requirements of ASTM F876-99a, ASTM F877-99a, CSA 137.5-99, DIN 16892 and all related standards. This system allows the compound to be extruded as a normal thermoplastic polymer, which will attain a high level of crosslinking in the processed form. The final product has all the improved properties associated with crosslinked polyethylene. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | DIN 53479, ASTM D1505 |
| Apparent Density | 0.51 | g/cm³ | DIN 53466 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 1.6 | g/10 min | Internal method |
| Moisture Content | % | Internal method | |
| Volatile Matter | % | Internal method | |
| Gel Content 1 | 72 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 22.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 200 | % | ISO 527-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 160 - 170 | °C | |
| Cylinder Zone 2 Temp. | 170 - 180 | °C | |
| Cylinder Zone 3 Temp. | 170 - 190 | °C | |
| Cylinder Zone 4 Temp. | 170 - 190 | °C | |
| Die Temperature | 190 - 220 | °C |
| Extrusion instructions |
|---|
| L/D: >25Compression ratio: 3:1 to 2.5 : 1Head: 200 to 210°CScrew: 70°C to 90 °C |
| Note Message | |
|---|---|
| 1 . | DIN 16892/ ASTM F 876-99a |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPC 6742 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Elvacite® 2008 | Lucite International Inc. | Acrylic (PMMA) | Elvacite® |
| Jampilen HP648S | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| Leona™ 14G25 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| PALMID® R 66 S GF 15 | pal plast GmbH | Nylon 66 | PALMID® |