NORYL™ PX9406K resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YcsHLO_NORYL-PX9406K-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL PX9406K resin may be suitable for consumer electronics applications. Flame retardant used is non-halogenated. UL94 V0 at 1.5 mm, 5VB at 2 mm, and 5VA at 2.5 mm. RTI (impact) = 105 C |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/10.0 kg | 7.00 | cm³/10min | |
| 280°C/5.0 kg | 11.0 | cm³/10min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2700 | MPa | ASTM D638 |
| -- | 2550 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 66.0 | MPa | ASTM D638 |
| Yield | 67.0 | MPa | ISO 527-2/50 |
| Break 3 | 50.0 | MPa | ASTM D638 |
| Break | 52.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.7 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/50 |
| Break 5 | 45 | % | ASTM D638 |
| Break | 55 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2650 | MPa | ASTM D790 |
| 6.40 mm | 2650 | MPa | ASTM D790 |
| -- 7 | 2420 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 104 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 100 | MPa | ASTM D790 |
| Yield, 6.40 mm | 101 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 100 | J/m | ASTM D256 |
| 23°C | 170 | J/m | ASTM D256 |
| -30°C 10 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 13 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 55.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 128 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 6.40 mm | 130 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 126 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 113 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 121 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 112 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 144 | °C | ISO 306/A120 |
| -- | 134 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | 110 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI Str | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.4E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Air) | 49 | kV/mm | ASTM D149 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, Testing by SABIC | V-0 | ||
| 2.00 mm, Testing by SABIC | 5VB | ||
| 2.50 mm, Testing by SABIC | 5VA | ||
| Glow Wire Flammability Index (1.50 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 800 | °C | |
| 2.00 mm | 800 | °C | |
| 3.00 mm | 800 | °C |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | ISO 11443 | ||
| 250°C, 1500 sec^-1 | 525 | Pa·s | |
| 260°C, 1500 sec^-1 | 390 | Pa·s | |
| 280°C, 1500 sec^-1 | 250 | Pa·s |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 243 to 293 | °C | |
| Middle Temperature | 254 to 299 | °C | |
| Front Temperature | 266 to 304 | °C | |
| Nozzle Temperature | 277 to 304 | °C | |
| Processing (Melt) Temp | 277 to 304 | °C | |
| Mold Temperature | 71.1 to 98.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 1206 LD | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| Nanjing Hongrui PA6 B1302 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| LUVOCOM® 80-8162 | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| Sylvin 7011EE-70 WHITE 1161 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 5170-85 Red 6290 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |