Durethan® AKV 35 H2.0 SR1 901510
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS Corporation |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YbMqIo_Durethan-AKV-35-H2-0-SR1-901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 35 % glass fibers, injection molding, heat-aging stabilized, improved surface finish |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.41 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ||||
| Across Flow : 300°C, 2.00 mm 1 | 1.0 | -- | % | ISO 294-4 |
| Across Flow : 120°C, 2 hr, 2.00 mm 2 | 0.090 | -- | % | ISO 294-4 |
| Flow : 300°C, 2.00 mm 3 | 0.32 | -- | % | ISO 294-4 |
| Flow : 120°C, 2 hr, 2.00 mm 4 | 0.070 | -- | % | ISO 294-4 |
| Across Flow : 300°C, 3.00 mm 5 | 1.4 | -- | % | ISO 2577 |
| Across Flow : 120°C, 2 hr, 3.00 mm 6 | 0.040 | -- | % | ISO 294-4 |
| Flow : 300°C, 3.00 mm 7 | 0.35 | -- | % | ISO 2577 |
| Flow : 120°C, 2 hr, 3.00 mm 8 | 0.030 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.8 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 11200 | 7500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 190 | 130 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 5.0 | % | ISO 527-2/5 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | 7000 | -- | MPa | |
| 1000 hr | 5800 | -- | MPa | |
| Flexural Modulus 9(23°C) | 10500 | 6700 | MPa | ISO 178/A |
| Flexural Stress 10 | ||||
| 3.5% Strain | -- | 170 | MPa | ISO 178/A |
| 23°C | 295 | 200 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 11(23°C) | 4.0 | 6.0 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GHR, 14-110, GF35 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 12 | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | 75 | kJ/m² | |
| 23°C | 80 | 90 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | < 10 | < 10 | kJ/m² | |
| -30°C | < 10 | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 65 | -- | kJ/m² | |
| 23°C | 75 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 230 | -- | °C | ISO 306/B120 |
| Melting Temperature 12 | 263 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.0E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 35 | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 4.00 | 10.0 | ||
| 23°C, 1 MHz | 4.00 | 4.00 | ||
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 0.011 | 0.21 | ||
| 23°C, 1 MHz | 0.015 | 0.065 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Flammability Index (2.00 mm) | 600 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 13 | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 150x150x3; MT 80°C; 400 Bar |
| 6 . | 150x150x3 |
| 7 . | 150x150x3; MT 80°C; 400 Bar |
| 8 . | 150x150x3 |
| 9 . | 2.0 mm/min |
| 10 . | 2.0 mm/min |
| 11 . | Pull Rate: 2 mm/min; 50% RH |
| 12 . | 10°C/min |
| 13 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SureSpec HP-020 | Genesis Polymers | PP Homopolymer | SureSpec |
| KOCETAL® K300LOBK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Lifoflex® UV 30 GB 1030 | ELASTO | SEBS | Lifoflex® |
| PIVINEL™ 108-0 | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |
| LNP™ COLORCOMP™ HF1130RC compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |