| SUMIKON® AM-100 type J black-B is a short glass fiber reinforced, non-flame retardant, diallyl phthalate molding compound. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.66 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.52 | % | JIS K6911 |
| Water absorption rate- by boiling | 0.19 | % | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 10300 | MPa | JIS K6911 |
| Flexural Strength | 135 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.2 | kJ/m² | JIS K6911 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 224 | °C | JIS K6911 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 13 | kV/mm | JIS K6911 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Insulation Resistance | JIS K6911 | ||
| -- 2 | 1.0E+15 | ohms | JIS K6911 |
| -- 3 | 2.0E+14 | ohms | JIS K6911 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.69 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B (step by step) |
| 2 . | As molded |
| 3 . | After boiling |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6MV14FR4K1681 | A. Schulman Inc. | Nylon 6 | SCHULAMID® |
| Telcar® SGI40011 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| Argothane® 18103 | Argotec LLC | TPU, Unspecified | Argothane® |
| EPO-TEK® T6067 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| WELLAMID Nylon 6000/58 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |