PRL NY66-GP2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YZEKqV_PRL-NY66-GP2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL NY66-GP2 is a Polyamide 66 (Nylon 66) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18 mm | 1.2 to 1.8 | % | |
| Across Flow : 3.18 mm | 1.5 to 2.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.18 mm) | 3380 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 89.6 | MPa | |
| Break, 3.18 mm | 89.6 | MPa | |
| Tensile Strain | ASTM D638 | ||
| Yield, 3.18 mm | 4.5 | % | |
| Break, 3.18 mm | 30 | % | |
| Flexural Modulus (3.18 mm) | 3030 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.8 | kJ/m² | |
| 23°C | 4.2 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 53 | J/m | ASTM D256 |
| 23°C | 3.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 246 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 102 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.9 to 85.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 271 to 282 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 277 to 293 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP520J | LyondellBasell Industries | PP Homopolymer | Moplen |
| Hanwha Total PE R908P | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| HANWHA EVA 2319 | Hanwha Chemical | EVA | HANWHA EVA |
| Keltan® 5465Q | LANXESS Buna GmbH | EPDM | Keltan® |
| Sylvin 2900-75 White 1482 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |