AKROMID® A3 GF 50 1 blue (3778)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YYMlt2_AKROMID-A3-GF-50-1-blue-3778-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GF 50 1 blue (3778) is a 50% glass fibre reinforced, heat stabilised polyamide 6.6 with very high rigidity and strength Applications are mainly components in mechanical engineering and in the automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.56 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16700 | 12600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 245 | 180 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 13500 | 13500 | MPa | ISO 178 |
| Flexural Stress 2 | 350 | 310 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 3.5 | -- | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 50 | -- | % | ISO 1172 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | -- | kJ/m² | |
| 23°C | 16 | 23 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 94 | -- | kJ/m² | |
| 23°C | 96 | 110 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 260 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 235 | -- | °C | ISO 75-2/C |
| Melting Temperature 4 | 262 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® PC 2812-UR | Plastic Solutions, Inc. | PC | PrimaFlex® |
| Unichem 8011K-02 | Colorite Polymers | PVC, Flexible | Unichem |
| Ferro PE NPE00IA04NA | Ferro Corporation | PE, Unspecified | Ferro PE |
| ELASTOSIL® R plus 4000/40 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| LEXAN™ EXL1433T resin | SABIC Innovative Plastics | PC | LEXAN™ |