3M™ Dyneon™ TFM™ Modified PTFE TFM 1700
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ TFM™ Modified PTFE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YXB1Ra_3M-Dyneon-TFM-Modified-PTFE-TFM-1700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Modified non free-flowing PTFE of the 2nd generation for compression moulding Features
Typical applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.16 | g/cm³ | ISO 12086 |
| Apparent Density | 0.41 | g/cm³ | ISO 60 |
| Molding Shrinkage | 5.6 | % | Internal Method |
| Average Particle Size | 25 | µm | ISO 13320 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | 15.0 | MPa | |
| Compression Molding Temperature | 23 to 26 | °C | |
| Sintering Temperature | 375 to 380 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 59 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 650 | MPa | ISO 527-2 |
| Deformation Under Load | ASTM D621 | ||
| 15 MPa 1 | 4.00 | % | |
| 15 MPa 2 | 9.00 | % | |
| 15 MPa 3 | 8.00 | % |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (100 µm) | 43.0 | MPa | ISO 527-3 |
| Tensile Elongation (Break, 100 µm) | 630 | % | ISO 527-3 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | DIN 53752 | ||
| 30 to 100°C | 1.2E-4 | cm/cm/°C | |
| 30 to 200°C | 1.4E-4 | cm/cm/°C | |
| 30 to 260°C | 1.7E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.22 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Electric Strength (0.100 mm) | 90 | kV/mm | ISO 12086 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | permanent |
| 2 . | 100 hr |
| 3 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMSTER PF310G6 | Polyram Ram-On Industries | PBT | RAMSTER |
| Hylex® P1010L | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| Karina IVORY PVC COMPOUND -E 845-35/ 2-CRM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| O'Tech OM 6737 | O'Tech Corporation | PVC, Unspecified | O'Tech |
| Zytel® PLUS PLS95G35DH1 NC010 | DuPont Performance Polymers | Nylon, Unspecified | Zytel® PLUS |