KOCETAL® K100
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOCETAL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YWc9Bp_KOCETAL-K100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Kocetal K100 is a high viscosity grade and suitable for extrusion and injection moldings. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 2.2 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60%RH) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 78 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 57.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 80 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2200 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 87 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 158 | °C | |
| 1.8 MPa, Unannealed | 110 | °C | |
| Vicat Softening Temperature | 162 | °C | ASTM D1525 |
| Melting Temperature | 166 | °C | |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Dielectric Constant | 3.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 6.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 180 to 190 | °C | |
| Front Temperature | 190 to 200 | °C | |
| Nozzle Temperature | 190 to 200 | °C | |
| Processing (Melt) Temp | < 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 78.5 | MPa | |
| Holding Pressure | 29.4 to 49.0 | MPa | |
| Back Pressure | 0.981 to 2.94 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS 722 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Mylar® MO 21 (1400 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| ELASTOSIL® 8100 N | Wacker Chemie AG | Silicone | ELASTOSIL® |
| Hyundai EP PPF HT340J | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| Plexiglas® Satinice df23 7H | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |