MAJORIS FW300 - 1335
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YVm2Lv_MAJORIS-FW300---1335.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FW300 - 1335 is a white, 30% mineral filled polypropylene compound intended for injection moulding. The product is available in natural (FW300) and black (FW300 - 8229) but other colours can be supplied on request. FW300 - 1335 is intended for component, which require very good surface quality, rigidity, low shrinkage and high dimensional stability. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 19 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.80 - 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 55 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 59.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 97.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 250 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trexprene® A65SCI | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Braskem PP EP 448S | Braskem | PP Impact Copolymer | Braskem PP |
| Delta PPR-1LG80 HSL | Delta Polymers | PP Homopolymer | Delta |
| Karina CREPE PVC COMPOUND TR-605-22/ 23 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SD POLYCA™ CR3241-10G | Sumika Styron Polycarbonate Limited | PC+PET | SD POLYCA™ |