OmniPro™ CPP 10M FR2
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniPro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YUBTgI_OmniPro-CPP-10M-FR2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame Resistant, Copolymer Polypropylene |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.978 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 24.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Flexural Modulus | 1170 | MPa | ASTM D790 |
| Flexural Strength | 33.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 85.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-2 | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 193 to 238 | °C | |
| Middle Temperature | 193 to 238 | °C | |
| Front Temperature | 193 to 238 | °C | |
| Nozzle Temperature | 193 to 238 | °C | |
| Processing (Melt) Temp | 193 to 238 | °C | |
| Mold Temperature | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® SX30CW | BASF Leuna GmbH | Nylon 66 | Miramid® |
| Generic PEK | Generic | PEK | Generic |
| KRATON® G1652 E | Kraton Polymers LLC | SEBS | KRATON® |
| Lumid® GP2150A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |
| LNP™ THERMOCOMP™ MF002S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |