Order Products : sales@su-jiao.com
Safrene® M 6650
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Safripol (PTY) LTD |
| Trademark: | Safrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YSSrd7_Safrene-M-6650.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Safrene® M 6650 High Density Polyethylene Resin is a high molecular mass grade specifically designed for extrusion blow moulding of containers greater than 20 liter capacity. It has a high melt viscosity and is primarily recommended for use on modern generation equipment. Safrene® M 6650 High Density Polyethylene Resin exhibits outstanding impact strength, high rigidity and good environmental stress-crack resistance. It is particularly suitable for drum applications between 50 liter and 250 liter and satisfies SABS 1176 requirements for the transportation of dangerous goods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.953 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 5.0 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.20 | g/10 min | ISO 1133 |
| Viscosity Number (Reduced Viscosity) | 450.0 | ml/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, molding | 26.0 | MPa | ISO 527-2/50 |
| Fracture, molding | 46.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, Compression Molded) | > 600 | % | ISO 527-2/50 |
| Flexural Stress (3.5% Strain, Compression Molded) | 21.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (-30°C, Compression Molded) | 35 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 80.0 | °C | ISO 306/B |
| Peak Crystallization Temperature (DSC) | 130 - 133 | °C | ISO 3146 |
| Additional Information |
|---|
| Blow Molding conditions: Feed Zone: 170 to 190°C Zone 1: 180 to 200°C Zone 2: 200 to 220°C Zone 3: 200 to 220°C Melt Temperature: 200 to 220°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 - 190 | °C | |
| Cylinder Zone 2 Temp. | 180 - 200 | °C | |
| Cylinder Zone 3 Temp. | 200 - 220 | °C | |
| Cylinder Zone 4 Temp. | 200 - 220 | °C | |
| Melt Temperature | 200 - 220 | °C |
| Note Message | |
|---|---|
| 1 . | Unannealed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PPA 7500 GF 50 H | TER HELL PLASTIC GMBH | PPA | TEREZ PPA |
| Estane® 2103-80PF TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| LEXAN™ GLX143 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Sylvin 8205-75UV Brown 7478 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® DP AKV 30 FN00 DUS013 000000 | LANXESS GmbH | Nylon 66 | Durethan® |