Luranyl® KR 2403 G2 TW 26343
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Luranyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YRmDEu_LuranylKR2403G2TW26343.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Luranyl®KR 2403 G2 TW 26343 is a polyphenylene ether + PS (PPE + PS) material, and the filler is 10% glass fiber reinforced material. This product is available in Europe, and the processing method is injection molding. Luranyl®The main features of KR 2403 G2 TW 26343 are:
Luranyl®The typical application fields of KR 2403 G2 TW 26343 are: water pipes/pipes/drinking water |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.14 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/21.6 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage (23°C, 3.20 mm) | 0.30 - 0.50 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | < 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5000 | MPa | ISO 527-2/1 |
| Tensile Stress (23°C) | 103 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 5.0 | % | ISO 527-2/5 |
| Flexural Stress 1(23°C) | 147 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 30 | kJ/m² | ISO 179/1eU |
| 23°C | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 141 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 80°C) | 5.0E-5 - 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.6 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) LP 340 | A. Schulman Europe | ABS | POLYMAN® |
| TECHNYL® eXten D 218 V30 BLACK | Solvay Engineering Plastics | Nylon 610 | TECHNYL® eXten |
| ELASTOSIL® LR 3003/60 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Axiall PVC 8247 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Sylvin 9077-80 Yellow 4161 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |