LNP™ STAT-KON™ FX98501 compound
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YRI1ww_LNP-STAT-KON-FX98501-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON FX98501 is a compound based on Polyethylene resin containing Proprietary Fillers. Added feature of this material is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-F-98501 Product reorder name: FX98501 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.09 | g/cm³ | ASTM D792 |
| -- | 1.08 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 4.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.019 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.021 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3350 | MPa | ASTM D638 |
| -- | 2740 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 39.0 | MPa | ASTM D638 |
| Yield | 36.0 | MPa | ISO 527-2/5 |
| Break 3 | 29.0 | MPa | ASTM D638 |
| Break | 32.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 5.9 | % | ASTM D638 |
| Yield | 5.7 | % | ISO 527-2/5 |
| Break 5 | 8.5 | % | ASTM D638 |
| Break | 7.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2230 | MPa | ASTM D790 |
| -- 7 | 2350 | MPa | ISO 178 |
| Flexural Stress | 45.8 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C 8 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 540 | J/m | ASTM D4812 |
| 23°C 9 | 32 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 11.7 | J | ASTM D3763 |
| -- | 4.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 118 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 114 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 88.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 85.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 9.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 to 4.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 210 to 221 | °C | |
| Front Temperature | 221 to 232 | °C | |
| Processing (Melt) Temp | 232 | °C | |
| Mold Temperature | 37.8 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9222-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Flontech® FT-CARR25-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Lanufene LLF 182H | Ras Lanuf Oil & Gas Processing Company (RASCO) | LLDPE | Lanufene |
| Hylon® N2213TL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Sylvin 83032-80UV Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |