TAIRILAC AG15A3
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAIRILAC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YQTV6S_TAIRILAC-AG15A3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FCFC ABS resin AG15A3 meets the requirements of UL, SGS and the certificates of environmental protection. |
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| 23°C | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 200°C/5.0 kg | 2.2 | g/10 min | ASTM D1238, ISO 1133 |
| 220°C/10.0 kg | 22 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class R, 23°C | 108 | ASTM D785 | |
| R scale, 23°C | 108 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 46.0 | MPa | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C) | 2650 | MPa | ASTM D790, ISO 178 |
| Flexural Strength (23°C) | 78.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 6.35 mm) | 220 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648, ISO 75-2/A | ||
| 1.8 MPa, unannealed, 12.7mm | 85.0 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, annealed 1 | 95.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 99.0 | °C | ISO 306/A, ASTM D1525 2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, All Colors) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 68.6 - 108 | MPa |
| Injection instructions |
|---|
| Screw Temperature: 190-230°C |
| Note Message | |
|---|---|
| 1 . | 80°Cx8Hr |
| 2 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A R 130/GF BLACK | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Sinvicomp SIM5029 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Nipol® LX111A2 | Zeon Corporation | Latex | Nipol® |
| Hostacom TRC 364N | LyondellBasell Industries | PP, Unspecified | Hostacom |
| LEXAN™ 104R resin | SABIC Innovative Plastics | PC | LEXAN™ |