| Fiber Reinforced - Electrically Conductive - EMI/RFI Shielding |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 - 0.40 | % | ASTM D955 |
| Moisture Content | 0.020 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay | sec | FTMS 101C 4046.1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6890 | MPa | ASTM D638 |
| Tensile Strength | 88.3 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.0 - 2.0 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 141 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 410 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 122 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | < 1.0E+4 | ohms | ASTM D257 |
| -- | < 1.0E+3 | ohms | ESD STM11.11 |
| Volume Resistivity | < 10 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -28.9 | °C | |
| Processing (Melt) Temp | 243 - 274 | °C | |
| Mold Temperature | 51.7 - 93.3 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps.Remove hopper magnets.Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYNEP® E4450 | Tyne Plastics LLC. | PET | TYNEP® |
| Daelim Po1y® LH-5540 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| ELASTOSIL® R 770/75 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| OPTUM® DPP40WI08GY | Ferro Corporation | Polyolefin, Unspecified | OPTUM® |
| Kinta NB2630G | Kinta Technology (Hong Kong) Co., Ltd. | PP, Unspecified | Kinta |