CERTENE™ HWF-0150
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YNgd9O_CERTENE-HWF-0150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HWF-0150 is a certified prime grade Hexene copolymer HIGH MOLECULAR WEIGHT developed for blown films. HWF-0150 can be used alone or in BLENDS with HMW-HDPE and/or LLDPE Blown film grades. HWF-0150 features UNIMODAL molecular weight distribution for improved processability at lower extruder pressure and good film stiffness. HWF-0150 can be used in a broad range of applications blended from 10% to 50% with either HMW-HDPE and/or LLDPE. HWF-0150 can be processed on HMW, high stalk film equipment with a die gap >0.75 to 1.25< mm.. HMF-0150 applications include industrial and trash can liners, as well as T-shirt bags. Recommended processing temperatures 195 to 205°C. HWF-0150 complies with FDR regulation 21CFR 177.1520 (c) 3.1 (a) + 3.2 (a) and with most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | < 0.10 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 12 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 12 µm | 26.0 | MPa | ASTM D882 |
| TD : Yield, 12 µm | 14.0 | MPa | ASTM D882 |
| MD : Break, 12 µm | 61.0 | MPa | ASTM D882 |
| TD : Break, 12 µm | 27.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 12 µm | 300 | % | ASTM D882 |
| TD : Break, 12 µm | 410 | % | ASTM D882 |
| Dart Drop Impact 1(12 µm) | 200 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 12 µm | 15 | g | ASTM D1922 |
| TD : 12 µm | 25 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 130 | °C | ASTM D3417 |
| Additional Information |
|---|
| Film Specimen: 0.5 mil (12 µm) film, melt temperature 410-440°F (210-225°C), blow-up-ratio 4.0:1, frost line height 5 x die ø. |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 2500-4 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Tufel® II 94305 | Momentive Performance Materials Inc. | Silicone | Tufel® II |
| CP PRYME® Nylon 6 N100MD2 | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| Gallonprene® GP310-8003 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| K-Prene GHT 45 | Technovinyl Polymers India Ltd. | TPE | K-Prene |