Ebalta GH 781 / GH 781 S
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YMVsvm_Ebalta-GH-781-GH-781-S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta GH 781 is a heat resistant two components epoxy resin with very low thermal expansion and high mechanical strength. ebalta GH 781 is suitable to pour on a cast aluminium carrier (sandblast surface). With a thickness of 10-20 mm you get a high quality surface with good thermal conductivity. With hardener GH 781 S a better curing and therefore shorter curing time is reached. For any amendments, repairs and sealings we also have a putty system available. By means of this system together with HRS hardener thicknesses of 5-6 mm can be reached. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | 0.050 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 87 to 93 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 9800 to 12800 | MPa | ISO 178 |
| Flexural Stress | 80.0 to 100 | MPa | ISO 178 |
| Compressive Stress | 135 to 155 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 6.0 to 8.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 113 to 119 | °C | ISO 75-2/B |
| CLTE - Flow | 3.5E-5 to 4.0E-5 | cm/cm/°C | DIN 53752 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 5.0 | ||
| Resin | Mix Ratio by Weight: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 2.60 to 2.80 | g/cm³ | |
| Viscosity (25°C) | 11 to 16 | Pa·s | |
| Curing Time (20°C) | 12 to 14 | hr | |
| Pot Life 1(20°C) | 90 to 110 | min |
| Note Message | |
|---|---|
| 1 . | 1000 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ NatureGran PV 6930 | TER HELL PLASTIC GMBH | PLA | TEREZ NatureGran |
| Addisil™ IND 2050 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| Asaflex™ 805 | AKelastomers | SBS | Asaflex™ |
| Fiberfil® J-60/30/E/HF | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| LNP™ STAT-KON™ RC008 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ STAT-KON™ |