| Message |
|---|
|
TPX®DX820 is a polymethylpentene copolymer (PMP copolymer) material,. This product is available in Europe or Asia Pacific region. The processing method is: extrusion coating. TPX®The main characteristics of DX820 are: hardness. TPX®The typical application areas of DX820 are: food contact applications |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.833 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 180 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1760 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 26.0 | MPa | ASTM D638 |
| 23°C | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 6.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1570 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 46.9 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 90.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 178 | °C | ASTM D1525 |
| Melting Temperature | 238 | °C | |
| CLTE - Flow | 3.8E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 63 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.12 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Clarity | 93.0 | ASTM D1746 | |
| Haze | 2.6 | % | ASTM D1003 |
| Additional Information |
|---|
| Unnotched Izod Impact, ASTM D256, 23°C: 8 kJ/m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V912A NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Multi-Flex® TPO 2503 S | Multibase, A Dow Corning Company | TPO (POE) | Multi-Flex® TPO |
| Neopor® 2400 | BASF Corporation | PS (EPS) | Neopor® |
| apilon 52bio® DB 40/AP | API SpA | TPU-Polyester | apilon 52bio® |
| PLUSTEK PB890 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |