Ketron® PEEK-CA30
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Ketron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YM8qUE_Ketron-PEEK-CA30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ketron® PEEK-CA30 is a Polyetheretherketone (PEEK) product filled with 30% carbon fiber. It is available in Europe. Typical application: Engineering/Industrial Parts. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.14 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 10.0 mm) | 102 | ISO 2039-2 | |
| Ball Indentation Hardness (10.0 mm) | 325 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7700 | MPa | ISO 527-2/1B/1 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2/1B/5 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/1B/5 |
| Compressive Stress | ISO 604/1 | ||
| 2% Strain | 97.0 | MPa | |
| 1% Strain | 49.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 230 | °C | ISO 75-2/A |
| Continuous Use Temperature | |||
| -- 1 | 250 | °C | |
| -- 2 | 310 | °C | |
| Melting Temperature (DSC) | 340 | °C | |
| CLTE - Flow | |||
| 23 to 100°C | 2.5E-5 | cm/cm/°C | |
| 23 to 150°C | 2.5E-5 | cm/cm/°C | |
| > 150°C | 5.5E-5 | cm/cm/°C | |
| Thermal Conductivity (23°C) | 0.92 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | < 1.0E+5 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Oxygen Index | 40 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 20000 hrs |
| 2 . | Short periods |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Delta N6-1G30 | Delta Polymers | Nylon 6 | Delta |
| Dynaprene® VE0087A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| Hostacom G3 R05 105555 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Karina WHITE COLOR CONCENTRATE MBU 10/ 70-IE | Karina Ind. e Com. de Plásticos Ltda | EVA | Karina |
| Karina IVORY PVC COMPOUND 753-35/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |