| 4DUR 23K22130 is a Standard Flow 30% Glass Fibre Reinforced PBT |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9000 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 215 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 210 | °C | ISO 306/B |
| Melting Temperature 2 | 225 | °C | ISO 11357 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 50 - 70 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SARANEX™ 553 | The Dow Chemical Company | PVDC | SARANEX™ |
| BJB Epoxy TC-1650 A/B | BJB Enterprises, Inc. | Epoxy | BJB Epoxy |
| Kepamid® 2300MR | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| Hyundai EP Breathable AT810/2102 | HYUNDAI EP Co., Ltd. | Polyolefin, Unspecified | Hyundai EP Breathable |
| LARIPUR® LPR 7015 | COIM S.p.A. | TPU-Polyester | LARIPUR® |