Triax® 2105
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | INEOS ABS (USA) |
| Trademark: | Triax® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YLGKu0_Triax-2105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Triax® 2105 resin is an injection molding grade of ABS (acrylonitrile butadiene styrene) modified with PC (polycarbonate) for high-heat applications. Triax 2105 provides high heat resistance, high impact strength and low emissions. Its consistent, clean, natural color makes it ideally suitable for use with color concentrates. Triax 2105 resin offers the right balance of properties for a variety of above-the-belt-line automotive applications or any application where higher temperature resistance and higher impact may be needed. As with any product, use of Triax 2105 resin in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 7.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Vertical flow direction | 0.60 - 0.80 | % | ISO 2577 |
| Flow direction | 0.60 - 0.80 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 47.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 45 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2100 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3 | ISO 180/1A | ||
| -30°C | 32 | kJ/m² | ISO 180/1A |
| 23°C | 43 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, not annealed | 108 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 91.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 105 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 5 | 38 | mm/min | SAE J369 |
| Carbon Emission | 13.0 | µg/g | VDA 277 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Dew Point - Desiccant Dryer | -28.9 | °C | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Shot Size | 50 - 75 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 238 - 254 | °C | |
| Middle Temperature | 243 - 260 | °C | |
| Front Temperature | 249 - 266 | °C | |
| Nozzle Temperature | 249 - 266 | °C | |
| Processing (Melt) Temp | 249 - 271 | °C | |
| Mold Temperature | 60.0 - 82.2 | °C | |
| Injection Pressure | 62.1 - 124 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | < 3.18 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Hold Pressure: 30 to 50% of Injection PressureScrew Speed: Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10.0-mm x 4.0-mm, 0.25-mm notch |
| 4 . | 4 mm |
| 5 . | (2 x 100 x 355 mm plaque |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene CC40P100-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| TRIPPS® 7A165 | Samyang Corporation | PPS | TRIPPS® |
| Cevian®-V 450SF | Daicel Polymer Ltd. | ABS | Cevian®-V |
| CYCOLOY™ RCX7233 resin | SABIC Innovative Plastics Asia Pacific | PC+ABS | CYCOLOY™ |
| LNP™ THERMOCOMP™ LC006 compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |