Torelina® A515
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Toray Resin Company |
| Trademark: | Torelina® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YKZ0Xi_Torelina-A515.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Torelina® A515 is a Polyphenylene Sulfide (PPS) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.68 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 0.85 | % | |
| Flow : 3.00 mm 2 | 0.20 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 145 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.6 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 12000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 220 | MPa | ISO 178 |
| Shear Strength (23°C) | 60.0 | MPa | JIS K7214 |
| Coefficient of Friction 3 | 0.15 | ||
| Taber Abrasion Resistance (1000 Cycles) | 50.0 | mg | ISO 9352 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| Melting Temperature | 278 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 2.4E-5 | cm/cm/°C | |
| Transverse | 3.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 26 | kV/mm | IEC 60243-1 |
| Dielectric Constant 4(23°C, 1 MHz) | 3.40 | IEC 60250 | |
| Dissipation Factor 5(23°C, 1 MHz) | 2.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.740 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 6(320°C, 1.00 mm) | 170 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | vs. Metal |
| 4 . | 60% RH |
| 5 . | 60% RH |
| 6 . | 98 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Scolefin 53 G 25-9 | Ravago Group | PP Copolymer | Scolefin |
| KumhoSunny PC 2203HI | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| POLYFLAM® RPP 2000 S | A. Schulman Europe | PP Homopolymer | POLYFLAM® |
| HIFOR® LF1021 | Westlake Chemical Corporation | LLDPE | HIFOR® |
| Sylvin 3210-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |