Iupilon® MB2212R
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YKRfpW_Iupilon-MB2212R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupilon® MB2212R is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® MB2212R are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Water Absorption (Saturation, 23°C) | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.4 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 46 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | 88.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 80 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 114 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 96.0 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 7.0E-5 | cm/cm/°C | |
| Transverse | 7.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 210 to 250 | °C | |
| Middle Temperature | 220 to 260 | °C | |
| Front Temperature | 230 to 270 | °C | |
| Nozzle Temperature | 230 to 270 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 121249 D | RTP Company | PLA | RTP |
| Karina SILVER MBATCH -E 47/ 35-GI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina WHITE PVC COMPOUD -E 836-10/132-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9812-65 Orange 594 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ DP003 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |